| 論文名 |
Control the wettability of poly(n-isopropylacrylamide-co-1-adamantan-1-ylmethyl acrylate) modified surfaces: the more Ada, the bigger impact? |
| 著者 |
Xiu-Juan Shi
Gao-Jian Chen
Yan-Wei Wang
Lin Yuan
Qiang Zhang
David M Haddleton
Hong Chen
|
| キーワード |
|
| 出版年月 |
1970年1月 |
| 発表先 |
Langmuir. 2013 Nov 19;29(46):14188-95. |
| WEBサイト |
|
| 論文概要（和文） |
ポリ（n-イソプロピルアクリルアミド-co-1-アダマンタン-1-イルメチルアクリレート）修飾表面の濡れ性を制御する：より多くのAda、より大きな影響？ |
| 論文概要（英文） |
Surface-initiated SET-LRP was used to synthesize polymer brush containing N-isopropylacrylamide and adamantyl acrylate using Cu(I)Cl/Me6-TREN as precursor catalyst and isopropanol/H2O as solvent. Different reaction conditions were explored to investigate the influence of different parameters (reaction time, catalyst concentration, monomer concentration) on the polymerization. Copolymers with variable 1-adamantan-1-ylmethyl acrylate (Ada) content and comparable thickness were synthesized onto silicon surfaces. Furthermore, the hydrophilic and bioactive molecule β-cyclodextrin-(mannose)7 (CDm) was synthesized and complexed with adamantane via host-guest interaction. The effect of adamantane alone and the effect of CDm together with adamantane on the wettability and thermoresponsive property of surface were investigated in detail. Experimental and molecular structure analysis showed that Ada at certain content together with CDm has the greatest impact on surface wettability. When Ada content was high (20%), copolymer-CDm surfaces showed almost no CDm complexed with Ada as the result of steric hindrance. |